Thin film transistor array panel and manufacturing method thereof

ABSTRACT

A thin film transistor array panel includes a substrate and a thin film transistor disposed on a surface of the substrate. The thin film transistor includes a semiconductor, a source electrode, and a drain electrode that are disposed on a same layer as one another. The semiconductor is between the source electrode and the drain electrode. The thin film transistor array panel further includes a buffer layer disposed between the semiconductor and the substrate and including an inorganic insulating material. The first edge of the buffer layer is substantially parallel to an adjacent edge of the semiconductor, a second edge of the buffer layer is substantially parallel to an adjacent edge of the source electrode, and a third edge of the buffer layer is substantially parallel to an adjacent edge of the drain electrode.

CROSS-REFERENCE TO RELATED APPLICATION

This application claims priority under 35 U.S.C. § 119 to Korean PatentApplication No. 10-2016-0054802 filed on May 3, 2016 in the KoreanIntellectual Property Office, the disclosure of which is incorporated byreference herein in its entirety.

TECHNICAL FIELD

One or more exemplary embodiments of the present inventive conceptrelate to a display device, and more particularly, to a thin filmtransistor array panel and a manufacturing method thereof.

DISCUSSION OF THE RELATED ART

A thin film transistor included in various electronic devices such as adisplay device includes a gate electrode electrically connected to agate line transmitting a scanning signal, a source electrodeelectrically connected to a data line transmitting a signal to beapplied to a pixel electrode, a drain electrode connected tothe sourceelectrode via a semiconductor channel.

The material used for the semiconductor channel affects the behavior andperformance of the thin film transistor. A semiconductor material may besilicon (Si), whichmay be an amorphous silicon or polysilicon, dependingon a crystallization type of the semiconductor. Amorphous silicon has asimple manufacturing process but has low charge mobility and may not besuitable for high performance opperations. On the other hand,polysilicon has high charge mobility, but crystalization is required. Anoxide semiconductor has higher electron mobility than an amorphoussilicon and a lower manufacturing cost than a polysilicon.

SUMMARY

According to an exemplary embodiment of the present inventive concept, athin film transistor array panel includes a substrate and a thin filmtransistor disposed on a surface of the substrate. The thin filmtransistor includes a semiconductor, a source electrode, and a drainelectrode that are disposed on a same layer as one another. Thesemiconductor is between the source electrode and the drain electrode.The thin film transistor array panel further includes a buffer layerdisposed between the semiconductor and the substrate and including aninorganic insulating material. The first edge of the buffer layer issubstantially parallel to an adjacent edge of the semiconductor, asecond edge of the buffer layer is substantially parallel to an adjacentedge of the source electrode, and a third edge of the buffer layer issubstantially parallel to an adjacent edge of the drain electrode.

In an exemplary embodiment of the present inventive concept, the thinfilm transistor further includes a gate electrode overlapping thesemiconductor and a gate insulator disposed between the gate electrodeand the semiconductor, and a boundary between the semiconductor and thesource electrode or a boundary between the semiconductor and the drainelectrode is substantially aligned with an adjacent side surface of thegate insulator extending in a direction substantially perpendicular to asurface of the substrate.

In an exemplary embodiment of the present inventive concept, the thinfilm transistor array panel further includes a light blocking filmdisposed between the buffer layer and the substrate. The light blockingfilm includes a part overlapping the buffer layer.

In an exemplary embodiment of the present inventive concept, the thinfilm transistor array panel further includes an interlayer insulatinglayer disposed on the thin film transistor and including an insulatingmaterial. The interlayer insulating layer includes a first contact holeon the drain electrode, and a second contact hole on the light blockingfilm.

In an exemplary embodiment of the present inventive concept, the lightblocking film has conductivity.

In an exemplary embodiment of the present inventive concept, a depth ofthe first contact hole and a depth of the second contact hole aresubstantially equal to each other.

In an exemplary embodiment of the present inventive concept, the thinfilm transistor array panel further includes a first connection partdisposed on the interlayer insulating layer and electrically connectedto the drain electrode through the first contact hole. The thin filmtransistor array panel additionally includes a second connection partdisposed on the interlayer insulating layer and electrically connectedto the light blocking film through the second contact hole.

In an exemplary embodiment of the present inventive concept, the firstconnection part and the second connection part are connected to eachother.

In an exemplary embodiment of the present inventive concept, the thinfilm transistor array panel further includes a passivation layerdisposed on the first and second connection parts. The passivation layerincludes a third contact hole on one of the first connection part andthe second connection part. The thin film transistor array panel furtherincludes a pixel electrode electrically connected to one of the firstconnection part and the second connection part through the third contacthole.

In an exemplary embodiment of the present inventive concept, the thinfilm transistor array panel further includes a gate conductor disposedat a same layer as the gate electrode and including substantially a samematerial as the gate electrode. The interlayer insulating layer includesa fourth contact hole on the gate conductor, and a depth of the fourthcontact hole is substantially the same as the depth of the first contacthole or the second contact hole.

According to an exemplary embodiment of the present inventive concept, amethod for manufacturing a thin film transistor array panel includesforming a buffer layer by depositing a first insulating material on asubstrate and forming a semiconductor layer by depositing and patterningan oxide semiconductor material on the buffer layer. The method formanufacturing a thin film transistor array panel further includesforming a gate insulating layer by depositing a second insulatingmaterial on the substrate and forming a gate conductive layer bydepositing a conductive material on the gate insulating layer. Themethod for manufacturing a thin film transistor array panel furtherincludes forming a photosensitive film pattern on the gate conductivelayer by coating the gate conductive layer with a photoresist andpatterning the photoresist through an exposure process using a mask. Themethod for manufacturing a thin film transistor array panel additionallyincludes etching the gate conductive layer by using the photosensitivefilm pattern as a mask to form a gate electrode. The method formanufacturing a thin film transistor array panel further includesetching the gate insulating layer by using the photosensitive filmpattern as a mask to form a gate insulator, and etching the buffer layerby using the semiconductor layer as a mask.

In an exemplary embodiment of the present inventive concept, etching thebuffer layer includes removing all sections of the buffer layer that arenot covered by the semiconductor layer.

In an exemplary embodiment of the present inventive concept, the methodfor manufacturing a thin film transistor array panel further includesforming a light blocking film on the substrate before forming the bufferlayer. A part of the light blocking film is exposed during the step ofetching the buffer layer.

In an exemplary embodiment of the present inventive concept, the methodfor manufacturing a thin film transistor array panel further includesforming a source electrode and a drain electrode from part of thesemiconductor layer.

In an exemplary embodiment of the present inventive concept, the methodfor manufacturing a thin film transistor array panel further includesforming an interlayer insulating layer by depositing a third insulatingmaterial on the substrate, forming a first contact hole exposing thedrain electrode by patterning the interlayer insulating layer through aphotolithography process using one photomask, and forming a secondcontact hole exposing the light blocking film by patterning theinterlayer insulating layer through the photolithography process usingthe one photomask.

In an exemplary embodiment of the present inventive concept, the methodfor manufacturing a thin film transistor array panel further includesforming a first connection part electrically connected to the drainelectrode through the first contact hole and by depositing andpatterning a conductive material on the substrate after patterning theinterlayer insulating layer. The method for manufacturing a thin filmtransistor array panel further includes forming a second connection partelectrically connected to the light blocking film through the secondcontact hole by depositing and patterning the conductive material on thesubstrate after patterning the interlayer insulating layer. The firstconnection part and the second connection part are connected to eachother.

In an exemplary embodiment of the present inventive concept, the methodfor manufacturing a thin film transistor array panel further includesforming a passivation layer on the substrate, forming a third contacthole exposing one of the first connection part and the second connectionpart by patterning the passivation layer, and forming a pixel electrodeon the passivation layer. The pixel electrode is electrically connectedto one of the first connection part and the second connection partthrough the third contact hole.

In an exemplary embodiment of the present inventive concept, theinterlayer insulating layer includes at least one among a silicon oxide(SiOx), a silicon nitride (SiNx), and a silicon oxynitride (SiON).

In an exemplary embodiment of the present inventive concept, the step offorming the source electrode and the drain electrode is partiallyperformed in at least one of the step of etching the gate insulatinglayer and the step of forming the interlayer insulating layer.

In an exemplary embodiment of the present inventive concept, the step offorming the source electrode and the drain electrode includes performinga plasma process on the semiconductor layer.

According to an exemplary embodiment of the present inventive concept, athin film transistor array panel includes a substrate and a thin filmtransistor disposed on the substrate and including a first layer. Thefirst layer includes a semiconductor, a source electrode, and a drainelectrode. The semiconductor is between the source electrode and thedrain electrode. The thin film transistor array panel further includes abuffer layer disposed between the first layer and the substrate andincluding an inorganic insulating material. A surface area of a bottomsurface of the first layer is greater than or equal to a surface area ofa top surface of the buffer layer.

In an exemplary embodiment of the present inventive concept, the surfacearea of the bottom surface of the first layer is greater than or equalto a surface area of a bottom surface of the buffer layer.

In an exemplary embodiment of the present inventive concept, the thinfilm transistor further includes a gate insulator disposed on thesemiconductor, and a boundary between the semiconductor and the sourceelectrode and a boundary between the semiconductor and the drainelectrode are each substantially aligned with a side surface of the gateinsulator extending in a direction perpendicular to the surface of thesubstrate.

In an exemplary embodiment of the present inventive concept, the thinfilm transistor array panel further includes a light blocking filmdisposed between the buffer layer and the substrate. The light blockingfilm overlaps the buffer layer.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and other features of the inventive concept will become moreapparent by describing in detail exemplary embodiments thereof, withreference to the accompanying drawing, in which:

FIG. 1 is a cross-sectional view of a thin film transistor array panelaccording to an exemplary embodiment of the present inventive concept;

FIG. 2 is a top plan view of the thin film transistor array panel shownin FIG. 1;

FIG. 3 and FIG. 4 are cross-sectional views of a thin film transistorarray panel according to an exemplary embodiment of the presentinventive concept;

FIGS. 5, 6, 7, 8, 9 and 10 are cross-sectional views sequentiallyshowing several steps of a manufacturing method of a thin filmtransistor array panel according to an exemplary embodiment of thepresent inventive concept;

FIG. 11 is a cross-sectional view of a display device including a thinfilm transistor array panel according to an exemplary embodiment of thepresent inventive concept;

FIG. 12 is a cross-sectional view of a display device including a thinfilm transistor array panel according to an exemplary embodiment of thepresent inventive concept; and

FIG. 13 is a plan view of the display device shown in FIG. 12 accordingto an exemplary embodiment of the present inventive concept.

DETAILED DESCRIPTION OF THE EMBODIMENTS

Exemplary embodiments of the present inventive concept will be describedmore fully hereinafter with reference to the accompanying drawings.

In the drawings, the thickness of layers, films, panels, regions, etc.,may be reduced or enlarged for clarity. Reference numerals that aresimilar or identical may designate similar or identical elements orfeatures throughout the specification and drawings. It will beunderstood that when an element such as a layer, film, region, orsubstrate is referred to as being “on” another element, it may bedirectly on the other element or intervening elements may also bepresent. In contrast, when an element is referred to as being “directlyon” another element, there are no intervening elements present.

Throughout this specification and the claims that follow, when it isdescribed that an element is “coupled” to another element, the elementmay be “directly coupled” to the other element or “electrically coupled”to the other element through a third element.

Now, a structure of a thin film transistor array panel and a method ofmanufacturing a thin film transistor array panel according to anexemplary embodiment of the present inventive concept will be describedin detail with reference to accompanying drawings.

The thin film transistor array panel according to an exemplaryembodiment of the present inventive concept will be described withreference to FIG. 1 and FIG. 2. FIG. 1 is the cross-sectional view ofthe thin film transistor array panel according to an exemplaryembodiment of the present inventive concept. FIG. 2 is a top plan viewof the thin film transistor array panel shown in FIG. 1; however, theplan view of the structure of the thin film transistor array panel shownin FIG. 1 is not limited to the plan view structure of FIG. 2.

Referring to FIG. 1, the thin film transistor array panel according toan exemplary embodiment of the present inventive concept includes asubstrate 110 and a thin film transistors TR positioned on the substrate110. However, it is understood that a plurality of thin film transistorsTR may be positioned on the substrate 110.

Referring to FIG. 1 and FIG. 2, a first direction D1 and a seconddirection D2 are parallel to a surface shown when viewing the surface ina direction perpendicular to a surface of the substrate 110 (e.g., aplan view of the substrate 110). In addition, the first and seconddirections D1 and D2 are perpendicular to each other. Further, a thirddirection D3 is perpendicular to the first and second directions D1 andD2 and is substantially perpendicular to the surface of the substrate110. The third direction D3 may be represented in a cross-sectionalstructure and is referred to as a cross-sectional direction. A structureshown by observing the surface parallel to the first direction D1 andthe second direction D2 in a direction substantially perpendicular tothe surface is referred to as a plan structure. In the cross-sectionalstructure, if a constituent element is positioned on any otherconstituent element, it means that two constituent elements are arrangedin the third direction D3, and other constituent elements may bepositioned between the two constituent elements.

The substrate 110 may include an insulating material such as plastic,glass, etc.

The thin film transistor TR includes a gate electrode 125, and asemiconductor 131, a source electrode 133, a drain electrode 135, and agate insulator 141 disposed between the semiconductor 131 and the gateelectrode 125.

The gate electrode 125 is electrically connected to a gate line, and mayreceive a gate signal including a gate-on voltage Von and a gate-offvoltage Voff. The gate electrode 125 may be disposed on the same layeras the gate line, and may include substantially the same material as thegate line.

The gate electrode 125 may be made of, for example, an aluminum-basedmetal of aluminum (Al) or aluminum alloys, a silver-based metal ofsilver (Ag) or silver alloys, a copper-based metal of copper (Cu) orcopper alloys, a molybdenum-based metal of molybdenum (Mo) or molybdenumalloys, chromium (Cr), tantalum (Ta), titanium (Ti), etc. However, thegate electrode 125 may include a multilayer structure including at leasttwo conductive layers having different physical properties from oneanother.

Referring to FIG. 1, the gate insulator 141 is disposed between thesemiconductor 131 and the gate electrode 125.

The gate insulator 141 may include an insulating material such as asilicon oxide (SiOx), a silicon nitride (SiNx), or a silicon oxynitride(SiON).

The gate insulator 141 may be a single layer or a multilayer structure,which may be a dual layer or more. When the gate insulator 141 is thesingle layer, the gate insulator 141 may include the insulating materialsuch as a silicon oxide (SiOx), a silicon nitride (SiNx), a siliconoxynitride (SiON), aluminum oxide (Al₂O₃), hafnium oxide (HfO₂ ), andyttrium oxide (Y₂O₃). When the gate insulator 141 is the multilayerstructure, a lowest layer of the multilayer facing the semiconductor 131may include an insulating oxide such as a silicon oxide (SiOx), aluminumoxide (Al₂O₃), hafnium oxide (HfO₃), and yttrium oxide (Y₂O₃), therebyimproving an interface characteristic of the semiconductor 131 andpreventing an impurity from penetrating the semiconductor 131. Inaddition to the lowest layer, at least one layer of the multilayerstructure that is positioned on the lowest layer of the multilayerstructure may include various insulating materials such as a siliconnitride (SiNx) and a silicon oxide (SiOx).

Referring to FIG. 1 and FIG. 2, a plane shape of the gate insulator 141is substantially the same as the plane shape of the gate electrode 125.Here, the plane shape means the plane shape of a surface ofcorresponding constituent element(s). In addition, an edge may be wheretwo surfaces (e.g. a side surface and an upper surface) connect to eachother and form an angle greater than zero at the connection (e.g. avertex). For example, an edge of the gate insulator 141 may be formed ata connection between its upper surface, which is substantially parallelto an upper surface of the substrate 110, and its side surface, whichextends in a direction substantially perpendicular to the upper surfaceof the substrate 110. For example, as shown in FIG. 2, an edge of thegate insulator 141 extending in the second direction D2, particularly,an edge of the upper surface, is substantially parallel to an adjacentedge of the gate electrode 125 extending in the second direction D2,particularly, an edge of the lower surface. That two edges aresubstantially parallel to one another means that two edges agree, arealigned with one another, overlap one another, or are parallel to oneanother within a predetermined distance even if they do not preciselymatch. Further, FIG. 1 and FIG. 2 show an example in which the edge ofthe gate insulator 141 is positioned more at the outer side than theadjacent edge of the lower surface of the gate electrode 125 and issubstantially parallel to the adjacent edge of the lower surface of thegate electrode 125 within the predetermined distance. For example, thegate insulator 141 may have a larger width than a width of the gateelectrode 125. This may be a result of the gate electrode 125 and thegate insulator 141 being formed by using the same photomask in amanufacturing process of the thin film transistor array panel.

The semiconductor 131 overlaps the gate electrode 125, and the gateinsulator 141 is disposed between the semiconductor 131 and the gateelectrode 125. Further, a channel of the thin film transistor TR isincluded in the semiconductor 131.

Referring to FIG. 1 and FIG. 2, the source electrode 133 and the drainelectrode 135 are positioned on opposite sides of the semiconductor 131and are separated from one another by the semiconductor 131. The sourceelectrode 133 and the drain electrode 135 are positioned atsubstantially the same layer as the semiconductor 131, and are eachdirectly connected to the semiconductor 131.

The source electrode 133, the drain electrode 135, and the semiconductor131 include substantially the same material (e.g., the same oxide). Theoxide included in the semiconductor 131, the source electrode 133, andthe drain electrode 135 may include a metal oxide such as one of zinc(Zn), indium (In), gallium (Ga), tin (Sn), and titanium (Ti), or acombination of the metals such as zinc (Zn), indium (In), gallium (Ga),tin (Sn), titanium (Ti), and the oxide thereof. For example, the oxideincluded in the semiconductor 131, the source electrode 133, and thedrain electrode 135 may include at least one among zinc oxide (ZnO),zinc-tin oxide (ZTO), zinc-indium oxide (ZIO), indium oxide (InO),titanium oxide (TiO), indium-gallium-zinc oxide (IGZO), andindium-zinc-tin oxide (IZTO).

A carrier concentration of the source electrode 133 and the drainelectrode 135 may be different from the carrier concentration of thesemiconductor 131. For example, when the carrier concentration of thesemiconductor 131 is less than 10 ¹⁸/cm³, the carrier concentration ofthe source electrode 133 and the drain electrode 135 may be greater thanor equal to 10 ¹⁸/cm³. A gradient region exists where the carrierconcentration gradually changes in a boundary between the sourceelectrode 133 and the semiconductor 131 and a boundary between the drainelectrode 135 and the semiconductor 131.

The source electrode 133 and the drain electrode 135 may include amaterial of an oxide semiconductor included in the semiconductor 131that includes the channel of the thin film transistor TR. The sourceelectrode 133 and the drain electrode 135 may further include the oxidesemiconductor included in the semiconductor 131 along with the materialof the oxide semiconductor. For example, the source electrode 133 andthe drain electrode 135 may further include at least one among fluorine(F), hydrogen (H), and sulfur (S) in addition to with the oxidesemiconductor included in the semiconductor 131. The concentration of atleast one among fluorine (F), hydrogen (H), and sulfur (S) included inthe source electrode 133 and the drain electrode 135 may have a carrierconcentration greater than or equal to 10 ¹⁵/cm³. In the boundarybetween the source electrode 133 and the semiconductor 131 and theboundary between the drain electrode 135 and the semiconductor 131, thegradient region, which is where the concentration of at least one amongfluorine (F), hydrogen (H), and sulfur (S) gradually changes, may exist.

The source electrode 133 and the drain electrode 135 may be formed byperforming plasma processing on the oxide semiconductor included in thesemiconductor 131. For example, the oxide semiconductor may be dopedwith a gas including at least one among fluorine (F), hydrogen (H), andsulfur (S) in a chamber to form the source electrode 133 and the drainelectrode 135 according to an exemplary embodiment of the presentinventive concept.

Accordingly, according to an exemplary embodiment of the presentinventive concept, the approximate plane shape of the semiconductor 131is substantially the same as the plane shape of the gate insulator 141.For example, with reference to FIG. 2, an edge of the semiconductor 131extending in a second direction D2, particularly an edge of the uppersurface, may be substantially parallel to an adjacent edge of the gateinsulator 141 extending in the second direction D2, particularly anadjacent edge of the lower surface. For example, the edge of thesemiconductor 131 extending in the second direction D2 may be alignedwith the adjacent edge of the gate insulator 141 extending in the seconddirection D2 such that the edge of the semiconductor 131 may be coveredby the adjacent edge of the gate insulator 141; however, exemplaryembodiments of the present inventive concept are not limited thereto. Inother words, with reference to FIG. 2, the boundary, between thesemiconductor 131 and the source electrode 133, extending in the seconddirection D2 or the boundary, between the semiconductor 131 and thedrain electrode 135, extending in the second direction D2 may besubstantially aligned with an adjacent edge of the gate insulator 141extending in the second direction D2, particularly an adjacent edge ofthe lower surface of the gate insulator 141. Alternatively, the boundarybetween the semiconductor 131 and the source electrode 133 or theboundary between the semiconductor 131 and the drain electrode 135 maybe positioned more towards an inside or an outside of the adjacent edgeof the gate insulator 141. In addition, the two boundaries mentionedabove may each be substantially parallel to an adjacent edge of the gateinsulator 141.

The gate insulator 141 covers most of the semiconductor 131. Forexample, the gate insulator 141 may cover the entire upper surface ofthe semiconductor 131.

According to an exemplary embodiment of the present inventive concept,the source electrode 133 and the drain electrode 135 may partiallyoverlap or not overlap the gate electrode 125 in the third direction D3.Accordingly, a parasitic capacitance between the gate electrode 125, andthe source electrode 133 or the drain electrode 135, may besignificantly reduced. As a result, kickback voltage, signal delay, anddistortion may be reduced.

An interlayer insulating layer 160 may be disposed on the thin filmtransistor TR. The interlayer insulating layer 160 may include theinorganic insulating material such as a silicon oxide (SiOx), a siliconnitride (SiNx), a silicon oxynitride (SiON), and silicon oxyfluoride(SiOF).

The interlayer insulating layer 160 may be a single layer or amultilayer structure, which may be a dual layer or more that includesdifferent materials. When the interlayer insulating layer 160 is thesingle layer structure, the interlayer insulating layer 160 may includethe inorganic insulating material such as a silicon oxide (SiOx), asilicon nitride (SiNx), a silicon oxynitride (SiON), and siliconoxyfluoride (SiOF), and particularly, may include at least one of asilicon nitride (SiNx) and a silicon oxynitride (SiON) for reducing theresistance of the source electrode 133 and the drain electrode 135 byinflowing hydrogen (H) in the source electrode 133 and the drainelectrode 135. When the interlayer insulating layer 160 is themultilayer structure, the lowest layer of the multilayer structure mayinclude at least one of a silicon nitride (SiNx) and a siliconoxynitride (SiON) for reducing the resistance of the source electrode133 and the drain electrode 135 by inflowing hydrogen (H) into thesource electrode 133 and the drain electrode 135. In addition, a middlelayer and an upper layer of the multilayer structure may include asilicon oxide (SiOx) that may be disposed on the lowest layer of themultiplayer structure. When the interlayer insulating layer 160 is themultilayer structure, another layer including material such as a siliconnitride (SiNx) or a silicon oxynitride (SiON) may be disposed on themiddle layer including a silicon oxide (SiOx).

The source electrode 133 and the drain electrode 135 may be formed to beconductive through a separate plasma processing after depositing theoxide semiconductor material on the substrate 110; however, a componentsuch as hydrogen included in a gas (e.g., silane (SiH₄) and ammonia(NH₃) used in a layer formation process of the interlayer insulatinglayer 160) may be doped into the semiconductor layer, thereby reducing aresistance. Alternatively, the component such as hydrogen included inthe interlayer insulating layer 160 may be diffused into thesemiconductor layer after forming the interlayer insulating layer 160,thereby reducing the resistance. Also, the source electrode 133 and thedrain electrode 135 may be doped with the component of an etch gas usedin a patterning process of the above-described gate insulator 141.

The interlayer insulating layer 160 may include a contact hole 163 onthe source electrode 133 and a contact hole 165 on the drain electrode135. For example, the contact hole 163 may penetrate the interlayerinsulating layer 160 and may expose a portion of the source electrode133, and the contact hole 165 may penetrate the interlayer insulatinglayer 160 and may expose a portion of the drain electrode 135. At leastone of the contact holes 163 and 165 may be omitted depending on a kindof the thin film transistor TR.

A data conductor including a first connection part 173 and a secondconnection part 175 is disposed on the interlayer insulating layer 160.The first connection part 173 is electrically connected to the sourceelectrode 133 of the thin film transistor TR through the contact hole163 of the interlayer insulating layer 160, and the second connectionpart 175 is electrically connected to the drain electrode 135 of thethin film transistor TR through the contact hole 165 of the interlayerinsulating layer 160. At least one of the first connection part 173 andthe second connection part 175 of the thin film transistor TR may beomitted depending on a kind of the thin film transistor TR.

A buffer layer 111 is disposed between the substrate 110 and thesemiconductor 131. The buffer layer 111 may prevent impurities fromflowing or permeating into the semiconductor 131 from the substrate 110,thereby protecting the semiconductor 131 and improving thecharacteristics of the semiconductor 131.

The buffer layer 111 may include the inorganic insulating material suchas a silicon oxide (SiOx), a silicon nitride (SiNx), aluminum oxide(Al₂O₃), hafnium oxide (HfO₃), and/or yttrium oxide (Y₂O₃).

The buffer layer 111 may be the single layer or the multilayerstructure, which may be a dual layer or more. For example, as shown inFIG. 1, when the buffer layer 111 is the dual layer, a lower layer 111 amay include a silicon nitride (SiNx) and an upper layer 111 b mayinclude a silicon oxide (SiOx).

Referring to FIG. 1, the plane shape of the buffer layer 111 issubstantially the same as the entire plane shape of the source electrode133, the semiconductor 131, and the drain electrode 135 that areconnected to one another. An edge of the buffer layer 111 extending inthe first direction D1, particularly an edge of the upper surface of thebuffer layer 111, may be substantially aligned with an adjacent edge ofthe source electrode 133, the semiconductor 131, and the drain electrode135 as a whole body extending in the first direction D1, particularly anadjacent edge of the lower surface. Further, FIG. 1 shows an exemplaryembodiment of the present inventive concept in which the edge of thebuffer layer 111 extending in the first direction D1 is positionedinside the adjacent edge of the entire lower surface of the sourceelectrode 133, the semiconductor 131, and the drain electrode 135extending in the first direction D1, and they are approximately parallelto each other within the predetermined distance. Alternatively, the edgeof the upper surface of the buffer layer 111 extending in the firstdirection D1 may be substantially aligned and matched with the adjacentedge of the entire lower surface of the source electrode 133, thesemiconductor 131, and the drain electrode 135 extending in the firstdirection D1, or the edge of the upper surface of the buffer layer 111may be positioned outside thereof. In other words, the buffer layer 111may be disposed under the source electrode 133, the semiconductor 131,and the drain electrode 135 of the thin film transistor TR. In addition,the upper surface of the substrate 110 that does not overlap the sourceelectrode 133, the semiconductor 131, and the drain electrode 135 in thethird direction D3 may directly contact the interlayer insulating layer160.

In an exemplary embodiment of the present inventive concept, the bufferlayer 111 may be disposed below the source electrode 133, thesemiconductor 131, and the drain electrode 135. A first side surface ofthe buffer layer 111 that is substantially perpendicular to thesubstrate 110 along the second direction D2 may be substantially alignedwith an adjacent side surface of the source electrode 133 along thesecond direction D2. In addition, a second side surface of the bufferlayer 111 that is substantially perpendicular to the substrate 110 alongthe second direction D2 may be substantially aligned with an adjacentside surface of the drain electrode 135 along the second direction D2.However, exemplary embodiments of the present inventive concept are notlimited thereto.

This thin film transistor array panel is the result of the buffer layer111 being etched by using the entire source electrode 133, semiconductor131, and drain electrode 135 as an etching mask in the manufacturingprocess of the thin film transistor array panel.

As described, according to an exemplary embodiment of the presentinventive concept, the buffer layer 111 disposed under the plurality ofthin film transistors TR disposed on the substrate 110 is patterned tohave substantially the same plane shape as a combined plane shape of thesource electrode 133, the semiconductor 131, and the drain electrode135, thereby being disposed under the source electrode 133,semiconductor 131, and drain electrode 135. Accordingly, a conditionsuch as the plane area and the shape of the buffer layer 111 disposedunder the semiconductor 131 may be uniform for the plurality of thinfilm transistors TR such that the amount of the impurity such ashydrogen (H) and/or oxygen (O) of the buffer layer 111 that is diffusedand flows or permeates into the semiconductor 131 is substantiallyuniform. Accordingly, the deviation of the characteristics of the thinfilm transistor TR due to the impurity flowing into or penetrating thesemiconductor 131, and the variation of the thin film transistor TRincluding the oxide semiconductor may be improved.

According to an exemplary embodiment of the present inventive concept,the upper surface of the source electrode 133 and the upper surface ofthe drain electrode 135 may have substantially the same height as theupper surface of the semiconductor 131. In addition, as shown in FIG. 1,the upper surface of the source electrode 133 and the upper surface ofthe drain electrode 135 may be slightly lower than the upper surface ofthe semiconductor 131. In the patterning process of the buffer layer111, the source electrode 133 and the drain electrode 135 that are notcovered by the gate insulator 141 may be exposed and slightly etchedsuch that the thickness of the source electrode 133 and the drainelectrode 135 in the third direction D3 may be less than a thickness ofthe semiconductor 131 in the third direction D3.

Further, the thin film transistor array panel according to an exemplaryembodiment of the present inventive concept will be described withreference to FIG. 3 and FIG. 4 as well as FIG. 1 and FIG. 2.

Referring to FIG. 3 and FIG. 4, the thin film transistor array panelaccording to an exemplary embodiment of the present inventive concept issimilar to most of the above-described exemplary embodiments of thepresent inventive concept except for a light blocking film 70 disposedbetween the substrate 110 and the buffer layer 111 for the thin filmtransistor TR.

The light blocking film 70 may block external light from reaching thesemiconductor 131, thereby preventing a characteristic deterioration ofthe semiconductor 131 and controlling a leakage of current from the thinfilm transistor TR. The light blocking film 70 may include a materialthat does not transmit the light of a wavelength band determined to beblocked, and for example, the light blocking film 70 may be made of theorganic insulating material, the inorganic insulating material, or theconductive material such as the metal. In addition, the light blockingfilm 70 may be formed of the single layer or the multilayer structure.In an exemplary embodiment of the present inventive concept, the lightblocking film 70 may include the conductive material.

The light blocking film 70 includes a portion that may overlap thebuffer layer 111 in the third direction D3 and a portion that might notoverlap the buffer layer. For example, the light blocking film 70 may bedisposed below the buffer layer 111.

In the case of a thin film transistor TR, the light blocking film 70 maybe omitted depending on several conditions such as a scenario wherelight is not irradiated under the substrate 110.

The interlayer insulating layer 160 may further include a contact hole166 on the light blocking film 70, and the data conductor may furtherinclude a third connection part 176 electrically connected to the lightblocking film 70 through the contact hole 166. For example, the contacthole 166 may penetrate the interlayer insulating layer 160 to the lightblocking film and may expose a portion of the light blocking film 70.The third connection part 176 may be disposed on the same layer as thesecond connection part 175, and as shown in FIG. 4, the third connectionpart 176 may be connected to the second connection part 175. The lightblocking film 70 may be applied with a voltage through the thirdconnection part 176.

According to an exemplary embodiment of the present inventive concept, aheight of the third connection part 176 extending from an upper surfaceof the interlayer insulating layer 160 to the upper surface of the lightblocking film 70 is substantially the same as a height of the firstconnection part 173 or the second connection part 175 extending from theupper surface of the interlayer insulating layer 160 to the uppersurface of the source electrode 133 or the drain electrode 135,respectively. The previously mentioned heights are substantially thesame because the buffer layer 111 is only positioned under the sourceelectrode 133, the semiconductor 131, and the drain electrode 135, andparticularly, the buffer layer 111 is removed around the contact hole166, which is different from a conventional art. Accordingly, a depth ofthe cross-sectional direction of the contact hole 166 on the lightblocking film 70 is substantially the same as a depth of thecross-sectional direction of the contact holes 163 and 165 on the drainelectrode 135 or the source electrode 133, respectively. Here, the depthmeans a depth in the third direction D3.

Accordingly, in the manufacturing process of the thin film transistorarray panel, the kind, the number, and the depth of the layers that thedifferent contact holes 163, 165 and 166 are penetrating to exposeconstituent elements (e.g., the source/drain electrodes 133 and 135 andthe light blocking film 70), are substantially the same such that thecontact holes 163, 165 and 166 may be simultaneously formed through aphotolithography process using one photomask. Accordingly, themanufacturing process may be simplified and the entire process may beenhanced. Also, the number of photomasks that may be used in themanufacturing process may be reduced such that the manufacturing timeand the manufacturing cost may be reduced. Also, it might not benecessary to use an etching gas having a high selectivity for the sourceelectrode 133, the drain electrode 135, and the buffer layer 111. Inaddition, damage that the source electrode 133 and the drain electrode135 or the semiconductor 131 may incur during the etching process forforming the contact hole may be reduced.

Referring to FIG. 3, a gate conductor 129 may be disposed on the samelayer as the gate electrode 125 and may be made of substantially thesame material as the gate electrode 125. Further, the gate conductor 129may be disposed on the substrate 110. In addition, a gate insulator 149and a buffer layer 119 having substantially the same plane shape as thegate conductor 129 may be disposed below the gate conductor 129. Forexample, the gate insulator 149 and the buffer layer 119 may be disposedon the substrate 110. In a plan view, an edge of the gate conductor 129extending in a second direction D2, particularly an edge of a lowersurface of the gate conductor 129, may be substantially parallel to anadjacent edge of the gate insulator 149, particularly an edge of anupper surface of the gate insulator 149. Further, an edge of the gateinsulator 149 and an adjacent edge of the buffer layer 119 may besubstantially aligned with one another. In an exemplary embodiment ofthe present inventive concept, a side surface of the buffer layer 119that is substantially perpendicular to the substrate 110 along thesecond direction D2 may be substantially aligned with an adjacent sidesurface of the gate insulator 149 along the second direction D2.Further, the gate insulator 149 may be disposed at the same layer as thegate insulator 141 and may be formed of substantially the same materialduring the same process. In addition, the buffer layer 119 may bedisposed at the same layer as the buffer layer 111 and may be formed ofsubstantially the same material during the same process.

The interlayer insulating layer 160 may further include a contact hole169 on the gate conductor 129. The contact hole 169 may be exposing aportion of the gate conductor 129. In addition, the data conductor mayfurther include a fourth connection part 179 electrically connected tothe gate conductor 129 through the contact hole 169.

Referring to FIG. 4, a passivation layer 180 may be disposed on theinterlayer insulating layer 160 and the data conductor (e.g., first,second, third and fourth connection parts 173, 175, 176 and 179). Thepassivation layer 180 may include at least one of the inorganicinsulating material and the organic insulating material, and thepassivation layer 180 may be formed of the single layer or themultilayer structure. Further, an upper surface of the passivation layer180 may be substantially flat.

The passivation layer 180 may include a contact hole 181 on the secondconnection part 175 or the third connection part 176. For example, thecontact hole 181 penetrates the passivation layer 180 and exposes aportion of the third connection part 176. In addition, the thirdconnection 176 may be electrically connected to the second connectionpart 175.

A pixel conductor including a pixel electrode 191 is disposed on thepassivation layer 180. The pixel electrode 191 may be electricallyconnected to the second connection part 175 or the third connection part176 through the contact hole 181. In this case, the second connectionpart 175 and the third connection part 176 may be electrically connectedto one another. Accordingly, the pixel electrode 191 is electricallyconnected to the drain electrode 135 of the thin film transistor TR,thereby receiving the data voltage.

Referring to FIG. 4, the light blocking film 70 may be electricallyconnected to the pixel electrode 191 and the drain electrode 135 throughthe third connection part 176, thereby receiving the data voltage. Asdescribed, if the light blocking film 70 is electrically connected tothe drain electrode 135 or the source electrode 133 of the thin filmtransistor TR to receive the voltage, a range of a change in current maybe small in a saturation region of a voltage-current characteristicgraph of the thin film transistor TR such that the characteristics ofthe current driving transistor may be improved.

Next, a manufacturing method of the thin film transistor according to anexemplary embodiment of the present inventive concept will be describedwith reference to FIG. 5 to FIG. 10 along with the above-describeddrawings. Here, the manufacturing method of the thin film transistorarray panel described in FIG. 3 will be described.

Referring to FIG. 5, the organic insulating material, the inorganicinsulating material, or the conductive material of the metal may bedisposed on the substrate 110 including the insulating material such asglass or plastic. Further, the organic insulating material, theinorganic insulating material, or the conductive material of the metalmay be patterned to form the light blocking film 70. In addition,according to an exemplary embodiment of the present inventive concept,to provide conductivity to the light blocking film 70, the conductivematerial may be deposited and patterned to form the light blocking film70. The light blocking film 70 may be omitted depending on the kind ofthin film transistor or the conditions of the thin film transistor arraypanel.

Referring to FIG. 6, the inorganic insulating material such as a siliconoxide (SiOx), a silicon nitride (SiNx), aluminum oxide (Al₂O₃), hafniumoxide (HfO₃), and yttrium oxide (Y₂O₃) may be disposed on the substrate110 formed with the light blocking film 70 by a method such as achemical vapor deposition to form a pre-buffer layer 111 p.

The oxide semiconductor material such as zinc oxide (ZnO), zinc-tinoxide (ZTO), zinc-indium oxide (ZIO), indium oxide (InO), titanium oxide(TiO), indium-gallium-zinc oxide (IGZO), and indium-zinc-tin oxide(IZTO) may be disposed and patterned on the pre-buffer layer 111 p toform a semiconductor layer 130.

Referring to FIG. 7, the inorganic insulating material such as a siliconoxide (SiOx), a silicon nitride (SiNx), or a silicon oxynitride (SiON)may be disposed on the substrate 110 to form a gate insulating layer140. In addition, the conductive material such as the metal may bedisposed on the gate insulating layer 140 to form a gate conductivelayer 120.

A photosensitive film such as a photoresist is coated on the gateconductive layer 120 and patterned through an exposure process using thephotomask to form photosensitive film patterns 50 and 51.

Referring to FIG. 8, the gate conductive layer 120 (e.g., as shown inFIG. 7) may be etched by using the photosensitive film patterns 50 and51 as the mask to form the gate electrode 125 and the gate conductor129. The gate conductive layer 120 may be etched by using, for example,wet etching or dry etching process.

Referring to FIG. 9, the gate insulating layer 140 (e.g., as shown inFIG. 8) may be etched by using the photosensitive film patterns 50 and51 as the mask to form the gate insulators 141 and 149. The gateinsulating layer 140 may be etched by using, for example, the dryetching process. In this process, the component of the etching gas suchas sulfur hexafluoride (SF₆) is doped into the semiconductor layer 130(e.g., as shown in FIG. 8) that is not covered by the photosensitivefilm patterns 50 and 51 and the gate insulator 141, thereby reducing theresistance of the exposed part of the semiconductor layer 130.Accordingly, the part of the semiconductor layer 130 covered by the gateinsulator 141 remains as the semiconductor 131. In addition, theremaining part of the semiconductor layer 130 that was not covered bythe gate insulator 141 has conductivity, thereby forming the sourceelectrode 133 and the drain electrode 135. However, exemplaryembodiments of the present inventive concept are not limited thereto,and most of the semiconductor layer 130 may also maintain itssemiconductor property in the patterning step to form the gateinsulators 141 and 149.

In the etching process of the gate insulating layer 140 or after theetching process of the gate insulating layer 140, the pre-buffer layer111 p may be etched by using the semiconductor layer 130 as a mask toform the buffer layers 111 and 119. Most of the pre-buffer layer 111 pdisposed below the semiconductor layer 130 may remain by using thesemiconductor layer 130 as the mask. Further, the pre-buffer layer 111 pthat is not covered by the semiconductor layer 130 is etched andremoved. Accordingly, the upper surface of the light blocking film 70and the substrate 110 that are not covered by the semiconductor layer130 may be exposed.

The semiconductor layer 130 that is not covered by the gate insulator141 and is exposed may be additionally processed to form the sourceelectrode 133 and the drain electrode 135. In this case, the processingmethod may include a heat treatment method in a reduced atmosphere, or aplasma process method using a gas plasma such as hydrogen (H₂), helium(He), phosphine (PH₃), ammonia (NH₃), silane (SiH₄), methane (CH₄),acetylene (C₂H₂), diborane (B₂H₆), carbon dioxide (CO₂), germane (GeH₄),hydrogen selenide (H₂Se), hydrogen sulfide (H₂S), argon (Ar), nitrogenN₂, nitrous oxide (N₂O), or fluoroform (CHF₃). In addition, thesemiconductor layer 130 covered by the gate insulator 141 maintains itssemiconductor property, thereby being the semiconductor 131.

Referring to FIG. 10, the inorganic insulating material such as asilicon oxide (SiOx), a silicon nitride (SiNx), and a silicon oxynitride(SiON) may be disposed on the substrate 110 formed with the gateelectrode 125 to form the interlayer insulating layer 160, which may bethe single layer or the multilayer structure. In this case, thecomponent such as hydrogen included in the gas, such as SiH₄ and NH₃,used in the layer formation process of the interlayer insulating layer160 may be doped into the semiconductor layer 130, the source electrode133 or the drain electrode 135, thereby forming the source electrode 133or the drain electrode 135. After the layer formation of the interlayerinsulating layer 160, the component such as hydrogen included in theinterlayer insulating layer 160 is diffused into the source electrode133 and the drain electrode 135, thereby reducing the resistance.

The interlayer insulating layer 160 may be patterned through thephotolithography process using one photomask and the etching process toform the contact hole 166 exposing the light blocking film 70, thecontact holes 163 and 165 respectively exposing the source electrode 133and the drain electrode 135, and the contact hole 169 exposing the gateconductor 129. In this case, even the contact holes 166, 163, 165 and169 exposing the constituent elements disposed at the different layerssuch as the light blocking film 70, the source and drain electrodes 133and 135, and the gate conductor 129 for at least one thin filmtransistor TR are etched to penetrate the interlayer insulating layer160 to substantially the same depth. Accordingly, the depths H1, H2, andH3 of the contact holes 166, 163, 165, and 169 extending in the thirddirection D3 are substantially the same. Thus, the time required for theetching may also be substantially the same.

Accordingly, the gas having the high etch selectivity might not berequired in an etching step of the contact holes 166, 163, 165, and 169.In addition, the damage to the source electrode 133 and the drainelectrode 135 may be reduced. Also, the plurality of contact holes 166,163, 165, and 169 exposing the constituent elements disposed atdifferent layers may be formed through one exposure process using onephotomask such that the number of photomasks may be reduced, therebyreducing the process steps and the variation in the process.

Depending on the kind of thin film transistor, at least one of thecontact hole 163 and the contact hole 165 might not be formed.

Referring to FIG. 3 as described above, the conductive material may bedisposed and patterned on the interlayer insulating layer 160 to formthe data conductor including the first connection part 173, the secondconnection part 175, the third connection part 176, and the fourthconnection part 179. Depending on the kind of the thin film transistor,at least one of the first connection part 173 and the second connectionpart 175 might not be formed. Also, when omitting the light blockingfilm 70, the contact hole 166 and the third connection part 176 may beomitted.

Referring to FIG. 4 as described above, in an exemplary embodiment ofthe present inventive concept, a passivation layer 180 may be formed bydisposing at least one of the inorganic insulating material and theorganic insulating material on the data conductor (e.g., first, second,third and fourth connection parts 173, 175, 176 and 179). Further, acontact hole 181 exposing either the second connection part 175 or thethird connection part 176 may be formed by patterning the passivationlayer 180. For example, the passivation layer 180 may be patternedthrough a photolithography process using a photomask.

FIG. 11 shows a display device including the thin film transistor arraypanel according to an exemplary embodiment of the present inventiveconcept.

The display device according to an exemplary embodiment of the presentinventive concept as an organic light emitting diode display may includethe same constituent elements as the thin film transistor array panelaccording to the above-described exemplary embodiments of the presentinventive concept. The same description for the above-described sameconstituent elements is omitted.

A pixel definition layer 360 may be formed on the passivation layer 180and the pixel electrode 191. Further, the pixel definition layer 360 maybe partially covering the pixel electrode 191. The pixel definitionlayer 360 includes an opening on the pixel electrode 191. The pixeldefinition layer 360 may be made of a resin such as a polyacrylate resinand a polyimide, a silica-based inorganic material, or the like.

An emission layer 370 may be disposed on the pixel electrode 191 in theopening of the pixel definition layer 360, and a common electrode 270may be disposed on the emission layer 370. The pixel electrode 191, theemission layer 370, and the common electrode 270 together form anorganic light emitting diode (OLED). The pixel electrode 191 forms ananode of the organic light emitting diode (OLED), and the commonelectrode 270 forms a cathode of the organic light emitting diode(OLED).

The light emitted from the emission layer 370 may be emitted from underthe substrate 110 and travel directly through the substrate 110 or afterseveral reflections, or may be emitted along the third direction D3 butnot through the substrate 110. For example, in the organic lightemitting diode (OLED) in which the light emitted from the emission layer370 is emitted in the third direction D3, the light blocking film 70 maybe omitted for all thin film transistors TR.

An encapsulation member, which may protect the organic light emittingdiode (OLED) from contaminants or external elements, may be disposed onthe common electrode 270.

FIG. 12 shows the display device including the thin film transistorarray panel according to an exemplary embodiment of the presentinventive concept, and FIG. 13 is a plan view corresponding to FIG. 12.FIG. 12 is a cross-sectional view of the thin film transistor arraypanel shown in FIG. 13 taken along a line B-B′ and B′-B″; however, theplane structure of the thin film transistor array panel having thecross-sectional structure like FIG. 12 is not limited to the planestructure shown in FIG. 13.

The display device as a liquid crystal display according to an exemplaryembodiment of the present inventive concept may include the sameconstituent elements as the thin film transistor array panel accordingto the above-described exemplary embodiments of the present inventiveconcept. The same description for the above-described same constituentelements is omitted.

A plurality of gate lines 121 connected to the gate electrode 125 may bedisposed on the substrate 110. The gate line 121 may be disposed on thesame layer as the gate electrode 125, and the gate line 121 may beformed of substantially the same material in the same process. The gateline 121 may extend in the first direction D1; however, it is notlimited thereto.

The gate insulator 141 may be disposed under the gate electrode 125 andthe gate line 121, and may include an edge extending, in a firstdirection D1, substantially parallel to an adjacent edge of the gateelectrode 125 and the gate line 121 extending in the first direction D1.In this case, the gate insulator 141 may have substantially the sameplane shape as the plane shape of the gate electrode 125 and a planeshape of the gate line 121.

Referring to FIG. 13, the gate electrode 125 may have a shape thatprotrudes upward or downward from the gate line 121 disposed on thesubstrate 110; however, exemplary embodiments of the present inventiveconcept are not limited thereto. In addition, the gate electrode 125 maybe partially included in the gate line 121.

The above-described gate conductor 129 may correspond to an end of thegate line 121.

The data conductor (e.g., first, second, third and fourth connectionparts 173, 175, 176 and 179) disposed on the interlayer insulating layer160 may further include a data line 171 crossing the gate line 121. Thedata line 171 may be connected to the first connection part 173. Thedata line 171 may extend in the second direction D2. The firstconnection part 173 may have a shape that extends to the data line 171,which extends in either a positive second direction D2 or a negativesecond direction D2; however, exemplary embodiments of the presentinventive concept are not limited thereto. In addition, the firstconnection part 173 may be partially included in the data line 171.

The pixel electrode 191 may include transparent conductive material suchas indium tin oxide (ITO) and indium zinc oxide (IZO).

A liquid crystal layer 3 including a plurality of liquid crystals 31 maybe disposed on the pixel electrode 191.

An insulating layer 210 sealing the liquid crystal layer 3 along withthe substrate 110 may be disposed on the liquid crystal layer 3. Theinsulating layer 210 may have a shape similar to a shape of thesubstrate 110.

An opposed electrode 280 may control an arrangement direction of theliquid crystals 31 by generating an electric field to the liquid crystallayer 3 and the pixel electrode 191. The opposed electrode 280 may bedisposed on or under the insulating layer 210. Alternatively, theopposed electrode 280 may be disposed between the substrate 110 and theliquid crystal layer 3. The opposed electrode 280 may include thetransparent conductive material such as ITO and IZO.

Alignment layers 11 and 21 may be disposed between the liquid crystallayer 3 and the pixel electrode 191, and between the liquid crystallayer 3 and the insulating layer 210, respectively. The alignment layers11 and 21 may control an initial alignment of the liquid crystal 31 whenthe electric field is not generated to the liquid crystal layer 3. Thealignment layers 11 and 21 may be close to the liquid crystal layer 3.

The display device as a non-emissive display device according to anexemplary embodiment of the present inventive concept may furtherinclude a backlight supplying the light. The backlight may be disposedunder the substrate 110.

Exemplary embodiments of the present inventive concept provide uniformcharacteristics to thin film transistors having the oxide semiconductor.Also, the present inventive concept resultantly enhances the quality ofthe thin film transistor array panel by reducing a number of photomasksused in a thin film transistor manufacturing process and by reducing aprocess variation.

The thin film transistor array panel according to an exemplaryembodiment of the present inventive concept may be included in variousdisplay devices.

While the present inventive concept has been particularly shown anddescribed with reference to exemplary embodiments thereof, it will beapparent to those of ordinary skill in the art that various changes inform and detail may be made thereto without departing from the spiritand scope of the present inventive concept.

What is claimed is:
 1. A thin film transistor array panel comprising: asubstrate; a thin film transistor disposed on a surface of the substrateand including a semiconductor, a source electrode, and a drain electrodethat are disposed on a same layer as one another, wherein thesemiconductor is between the source electrode and the drain electrode; abuffer layer disposed between the semiconductor and the substrate andincluding an inorganic insulating material, wherein a first edge of thebuffer layer is substantially parallel to an adjacent edge of thesemiconductor, a second edge of the buffer layer is substantiallyparallel to an adjacent edge of the source electrode, and a third edgeof the buffer layer is substantially parallel to an adjacent edge of thedrain electrode; a light blocking film disposed between the buffer layerand the substrate; a gate conductor disposed on the substrate; aninterlayer insulating layer disposed on the thin film transistor andincluding a first contact hole overlapping the drain electrode, a secondcontact hole overlapping the light blocking film and a third contacthole overlapping the gate conductor, wherein a depth of the thirdcontact hole is substantially the same as a depth of the first contacthole or a depth of the second contact hole.
 2. The thin film transistorarray panel of claim 1, wherein the thin film transistor furtherincludes a gate electrode overlapping the semiconductor and a gateinsulator disposed between the gate electrode and the semiconductor, anda boundary between the semiconductor and the source electrode or aboundary between the semiconductor and the drain electrode issubstantially aligned with an adjacent side surface of the gateinsulator extending in a direction substantially perpendicular to thesurface of the substrate.
 3. The thin film transistor array panel ofclaim 2, wherein the light blocking film includes a part overlapping thebuffer layer.
 4. The thin film transistor array panel of claim 3,wherein the interlayer insulating layer includes an insulating material.5. The thin film transistor array panel of claim 4, wherein the lightblocking film has conductivity.
 6. The thin film transistor array panelof claim 5, wherein a depth of the first contact hole and a depth of thesecond contact hole are substantially equal to each other.
 7. The thinfilm transistor array panel of claim 6, further comprising: a firstconnection part disposed on the interlayer insulating layer andelectrically connected to the drain electrode through the first contacthole; and a second connection part disposed on the interlayer insulatinglayer and electrically connected to the light blocking film through thesecond contact hole.
 8. The thin film transistor array panel of claim 7,wherein the first connection part and the second connection part areconnected to each other.
 9. The thin film transistor array panel ofclaim 8, further comprising: a passivation layer disposed on the firstand second connection parts, wherein the passivation layer includes afourth contact hole on one of the first connection part and the secondconnection part; and a pixel electrode electrically connected to one ofthe first connection part and the second connection part through thefourth contact hole.
 10. The thin film transistor array panel of claim6, wherein the gate conductor is disposed at a same layer as the gateelectrode and includes substantially a same material as the gateelectrode.
 11. A thin film transistor array panel comprising: asubstrate; a thin film transistor disposed on the substrate andincluding a first layer, wherein the first layer includes asemiconductor, a source electrode, and a drain electrode, wherein thesemiconductor is between the source electrode and the drain electrode;and a buffer layer disposed between the first layer and the substrateand including an inorganic insulating material, wherein a surface areaof a bottom surface of the first layer is greater than a surface area ofa top surface of the buffer layer, wherein the source electrode extendsbeyond a first edge of the buffer layer that is adjacent the sourceelectrode, and the drain electrode extends beyond a second edge of thebuffer layer that is adjacent the drain electrode.
 12. The thin filmtransistor array panel of claim 11, wherein the surface area of thebottom surface of the first layer is greater than or equal to a surfacearea of a bottom surface of the buffer layer.
 13. The thin filmtransistor array panel of claim 12, wherein the thin film transistorfurther includes a gate insulator disposed on the semiconductor, and aboundary between the semiconductor and the source electrode and aboundary between the semiconductor and the drain electrode are eachsubstantially aligned with a side surface of the gate insulatorextending in a direction perpendicular to a surface of the substrate.14. The thin film transistor array panel of claim 13, further comprisinga light blocking film disposed between the buffer layer and thesubstrate, wherein the light blocking film overlaps the buffer layer.15. The thin film transistor array panel of claim 11, wherein the bufferlayer includes a first layer and a second layer disposed on the firstlayer of the buffer layer, and the second layer is aligned with thefirst layer of the buffer layer.